ARONIX® 400-800 mPa·s UV Curable Adhesive
ARONIX® 400-800 mPa·s UV Curable Adhesive
SKU:ULT-896ad4
Solvent-free UV adhesive with 400-800 mPa·s viscosity, exceptional adhesion & heat resistance for diverse applications.
Regular price
$24.99
Regular price
Sale price
$24.99
Unit price
per
Initiate Order
ARONIX® 400-800 mPa·s UV Curable Adhesive
$24.99
Quantity: 1
Claim Your Seller Account
ARONIX® 400-800 mPa·s UV Curable Adhesive
$24.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The ARONIX® 400-800 mPa·s Viscosity UV Curable Adhesive offers a solvent-free solution with low viscosity and exceptional adhesion to various substrates. Its yellowing resistance due to heat and UV rivals industry standard UVX-5457, providing reliability in diverse applications. With a Glass Transition Temperature (Tg) of 6ºC and impressive peel strengths on different substrates, this adhesive ensures secure bonding for demanding projects. Ideal for UV curing under specific conditions, such as Metal Halide exposure at 240 W/cm, this adhesive guarantees optimal performance.
Product Specifications
180 Degree Peel Strength Glass 180 Degree Peel Strength
25 N/in
180 Degree Peel Strength Note For 180 Degree Peel Strength
Sample structure: PET (Surface treatment)/UV Curable Adhesives (10 μm)/Glass180 degree Peel Strength: 23ºC, 200 mm/min.
Note Note
Photo Curing Conditions: Metal Halide, 240 W/cm, 1,200 mJ/cm² (UV-A)Surface treatment: Corona discharge treatment
Specifications Glass Transition Temperature Tg
6 ºC
Specifications Viscosity At 25 Degree Celsius C Temperature
400 to 800 mPa·s
T Peel Strength Cyclic Olefin Polymer Cop T Peel Strength Surfac
13 N/in
T Peel Strength Note For T Peel Strength
Sample structure: Various Substrates/UV Curable Adhesives(10 μm)/ Various SubstratesT-Peel Strength: 23ºC, 200 mm/min.
T Peel Strength Polycarbonate Pc T Peel Strength
13 N/in
T Peel Strength Polyethylene Terephthalate Pet T Peel Strength S
16 N/in
T Peel Strength Poly Methyl Methacrylate Pmma T Peel Strength
14 N/in
T Peel Strength Tantalum Carbides Tac T Peel Strength
10 N/in