Get superior adhesion & transparency with ARONIX® UV Curable Adhesive - ideal for optical applications. Low water absorption & exceptional bonding strength.
Regular price
$29.99
Regular price
Sale price
$29.99
Unit price
per
Initiate Order
ARONIX® UV Curable Adhesive
$29.99
Quantity: 1
Claim Your Seller Account
ARONIX® UV Curable Adhesive
$29.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The ARONIX® 163 mPa·s Viscosity UV Curable Adhesive is a top-tier solution for bonding various substrates with exceptional adhesion. With a low glass transition temperature of 18ºC and minimal water absorption at 1.7%, this adhesive excels in optical applications thanks to its colorless transparency. The product offers robust adhesion to materials like PET, PMMA, PC, TAC, polyimide, and glass, meeting stringent industry standards for quality and durability.
Product Specifications
180 Degree Peel Strength Glass 180 Degree Peel Strength
14 N/in
180 Degree Peel Strength Note For 180 Degree Peel Strength
Sample structure: PET (Adhesive Type)/UV Curable Adhesives(10-15 µm)/Various SubstratesPET (Adhesive Type): COSOMOSHINE® A4300 (TOYOBO, 50 µm)Various SubstratesPET ï¼LUMIRROR® T-60 (TORAY, 50 µm, Non-Adhesive Type)PMMA: ACRYLITE®#001; (MITSUBISHI RAYON, 1 mm)PC: IUPILON® NF-2000 (MITSUBISHI ENGINEERING-PLASTICS, 1 mm)TAC: FUJITAC® TD 80UL (FUJIFILM, 80 µm)Polyimide: KAPTON® 100EN (DU PONT-TORAY, 25 µm)Glass: FLOAT GLASS (NIPPON SHEET GLASS, 3 mm)Photo Curing Conditions: Metal Halide, 160 W/cm, 1,000 mJ/cm² (UV-A)180º Peel Strength: 23ºC, 200 mm/min.
180 Degree Peel Strength Polycarbonate Pc 180 Degree Peel Streng
22 N/in
180 Degree Peel Strength Polyethylene Terephthalate Pet 180 Degr
16 N/in
180 Degree Peel Strength Polyimide Pi 180 Degree Peel Strength
19 N/in
180 Degree Peel Strength Poly Methyl Methacrylate Pmma 180 Degre
22 N/in
180 Degree Peel Strength Tantalum Carbides Tac 180 Degree Peel S
22 N/in
Note Note
Water absorption = ï¼W2ï¼W1ï¼/W1 x 100 (%)W1 ï¼initial weight after drying for 24 h at 50ºC, W2ï¼weight after soaking in water for 24 h at 23ºC
Specifications Glass Transition Temperature Tg
18 ºC
Specifications Viscosity At 25 Degree Celsius C Temperature
163 mPa·s
Specifications Water Absorption Of Cured Resin
1.7 %