1.750 Inch Hastelloy X Alloy Bar
1.750 Inch Hastelloy X Alloy Bar
SKU:HAS-026ebe
Highly durable 1.750 Inch Hastelloy X (HX) Alloy Bar with exceptional high temperature strength, oxidation resistance, and versatile applications.
Regular price
$129.99
Regular price
Sale price
$129.99
Unit price
per
Initiate Order
1.750 Inch Hastelloy X Alloy Bar
$129.99
Quantity: 1
Claim Your Seller Account
1.750 Inch Hastelloy X Alloy Bar
$129.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The 1.750 Inch Hastelloy X (HX) Alloy Bar offers exceptional high temperature strength and oxidation resistance up to 2200 °F. With superior forming and welding capabilities, this alloy is ideal for applications in petrochemical processes, gas turbines, industrial furnaces, and aerospace components. Its composition, meeting UNS N06002 standards, includes Nickel (Ni) 47.5%, Chromium (Cr) 21.8%, Iron (Fe) 18.5%, and Molybdenum (Mo) 9%, ensuring resistance to diverse atmospheres and stress-corrosion cracking. Certified to AMS and other industry-specific standards, this alloy is a reliable choice for critical environments.
Ready to Grow Without Cash Flow Constraints?
Product Specifications
Additional Information Additional Information
A wrought nickel base alloy with excellent high temperature strength and oxidation resistance. All of the product forms are excellent in terms of forming and welding. Although this alloy is primarily noted for heat and oxidation resistance it also has good resistance to chloride stress-corrosion cracking and has good resistance to carburization, excellent resistance to reducing or carburizing atmospheres. Alloy X is one of the most widely used nickel base super alloys for gas turbine engine components.AMS 5754 has no yield or tensile strength requirements, but it does require a hardness maximum and stress rupture minimums. Strong and Oxidation Resistant to 2200 ºF (1200 ºC) - Hastelloy® alloy X is a solid solution strengthened grade has good strength and oxidation resistance up to 2200 ºF (1200 ºC).
Applications 0
The alloy finds use in petrochemical process equipment and gas turbines in the hot combustor zone sections. Also used for structural components in industrial furnace applications because of the excellent oxidation resistance.Hastelloy® alloy X is recommended especially for use in furnace applications because it has unusual resistance to oxidizing, reducing, and neutral atmospheres. Furnace rolls made of this alloy were still in good condition after operating for 8700 hours at 2150 ºF. Furnace trays, used to support heavy loads, have been exposed to temperatures up to 2300 ºF. in an oxidizing atmosphere without bending or warping. Alloy X is equally suitable for use in jet engine tailpipes, afterburner components, turbine blades, nozzle vanes, cabin heaters, and other aircraft parts. Gas turbine combustion cans and ducting, heat-treating equipment.Alloy X has wide use in gas turbine engines for combustion zone components such as transition duct, combustor cans, spray bars and flame holders as well as in afterburners, tailpipes and cabin heaters. It is recommended for use in industrial furnace applications because it has unusual resistance to oxidizing, reducing and neutral atmospheres. Furnace rolls of this alloy were still in good condition after operating for 8700 hours at 2150 ºF (1177 ºC). Hastelloy® alloy X is also used in the chemical process industry for retorts, muffles, catalyst support grids, furnace baffles, tubing for pyrolysis operations and flash drier components.
General Resistance Barrod Usa
AMS 5754 | B472
General Resistance Forging Usa
B564
General Resistance General Resistance
Temperature | Oxidation
General Resistance Sheetplate Usa
AMS 5536 | B435
General Resistance Unified Numbering System Uns
N06002
General Resistance Weld Electrode
A5.11 ENiCrMo-2
General Resistance Weld Wire
A5.14 ERNiCrMo-2
General Resistance Werkstof
2.4665
Mechanical Elongation
45.5 %
Mechanical Hardness
B90
Mechanical Mechanical Type
Annealed
Mechanical Tensile Strength
115 ksi
Mechanical Yield Strength
50 ksi
Nominal Chemistry Carbon C
0.1
Nominal Chemistry Chromium Cr
21.8
Nominal Chemistry Cobalt Co
1.5
Nominal Chemistry Iron Fe
18.5
Nominal Chemistry Manganese Mn
0.5
Nominal Chemistry Molybdenum Mo
9
Nominal Chemistry Nickel Ni
Balanced
Nominal Chemistry Other
0.1
Nominal Chemistry Silicon Si
0.5
Nominal Chemistry Tungsten W
0.6
Physical Density
0.305 lb/in³
Physical Electrical Resistivity
680.9 ohm/cir-mil-ft
Physical Melting Range
2300 to 2470 ºF
Physical Specific Heat
0.100 Btu/lb ºF
Physical Thermal Expansion Coefficient At 79 To 200 Degree Fahre
7.7 x 10-6 in/in/ºF
Specifications Alloy
HX
Specifications Size
1.750 in
Specifications Type
Bar