1mm Aluminum/Silicon Alloy Wire
1mm Aluminum/Silicon Alloy Wire
SKU:ALU-ec2cf3
High-quality 1mm Aluminum/Silicon Alloy Wire with a 310.00 MPa tensile strength and 2.6-3.5 µΩ·cm electrical resistivity, perfect for various applications.
Regular price
$25.99
Regular price
Sale price
$25.99
Unit price
per
Initiate Order
1mm Aluminum/Silicon Alloy Wire
$25.99
Quantity: 1
Claim Your Seller Account
1mm Aluminum/Silicon Alloy Wire
$25.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The 1mm Aluminum/Silicon Alloy Wire by Goodfellow Corp. is a high-quality, hard-temper wire suitable for various applications. With a tensile strength of 310.00 MPa and electrical resistivity ranging from 2.6 to 3.5 µΩ·cm, this wire offers reliable performance. Meeting industry standards for alloys, this product is ideal for projects requiring precise specifications and durability.
Product Specifications
Electrical Properties Electrical Resistivity
2.6 to 3.5 µΩ·cm
Electrical Properties Temperature Coefficient
0.00420 k-1
Material Material
Aluminum/SiliconAlloys are mixtures of a metal with other elements, the precise combination being governed by the required properties. Alloys are generally considered to be metallic in nature i.e. they have good thermal and electrical conductivities).Alloys can be manufactured by various routes, the most widely used being to melt the constituents together and to cool the resultant mixture to form a single or multi-phase solid.
Mechanical Properties Tensile Strength
310.00 MPa
Physical Properties Density
2.700 g·cm-3
Specifications Diameter
1 mm
Specifications Form
Wire
Specifications Length
1 to 20 m
Specifications Temper
Hard
Thermal Properties Melting Point
600.00 ºC
Tolerances Diameter Tolerance
10 %
Tolerances Length Round Tolerance
-1 % | +5 %
Type Type
AlloyAlloys are mixtures of a metal with other elements, the precise combination being governed by the required properties. Alloys are generally considered to be metallic in nature i.e. they have good thermal and electrical conductivities). Alloys can be manufactured by various routes, the most widely used being to melt the constituents together and to cool the resultant mixture to form a single or multi-phase solid.
Analysis Copper Cu
30 ppm
Analysis Iron Fe
60 ppm
Analysis Manganese Mn
30 ppm