Carbon Nanotube Composite HIPS - 49 Rockwell Hardness L-Scale
Carbon Nanotube Composite HIPS - 49 Rockwell Hardness L-Scale
SKU:HIG-ecc2b6
Boost durability with our 49 Rockwell Hardness L-Scale Carbon Nanotube Composite for electronic and automotive needs.
Regular price
$29.99
Regular price
Sale price
$29.99
Unit price
per
Initiate Order
Carbon Nanotube Composite HIPS - 49 Rockwell Hardness L-Scale
$29.99
Quantity: 1
Claim Your Seller Account
Carbon Nanotube Composite HIPS - 49 Rockwell Hardness L-Scale
$29.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
Enhance your electronic and automotive parts' durability with our 49 Rockwell Hardness L-Scale High Impact Polystyrene (HIPS) Carbon Nanotube (CNT) Composite. With a low conductive filler content, it preserves resin-specific properties while offering excellent electrical conductivity, strength, and thermal stability. Ideal for Li-ion battery additives, tire treads, and more, our product ensures superior performance and longevity. Backed by ASTM standards, this composite is a reliable choice for demanding applications.
Product Specifications
Additional Information
When producing sheet and tray, physical property of resin is well maintained without breaking, and formability and deformability are excellent.Compound products with high content of mineral fillers such as CB inhibit resin-specific properties which lead to easy breaking when producing sheet and tray.CNT is known as having excellent electrical conductivity, thermal conductivity, strength, and thermal stability. Demand for Li-ion Battery as positive electrode conductive additives has been increasing and CNT is also being used in applications such as tire treads and antistatic resins.Kumho's CNT have a highly oriented bundle structure and have been used by major battery manufacturers and tire manufacturers globally. Multiple grades of CNT are available depending on required property and each application, and we also have various types of rubber and resin compound and masterbatches.Kumho Petrochemical with one of the world's largest synthetic rubber manufacturing capacities was established in 1970 and developing their business in several fields including synthetic resins, specialty chemicals, nanocarbons, energy, and building materials.Major application with Kumho's CNTLi-ion Battery as positive electrode conductive additives for automotiveTire treadsElectronic Parts TraysConductive coatingElectro-Magnetic Interference (EMI) Shielding CompositeConductive resin/rubber
Applications Applications
Carrier Tape | Sheets | Thermoformed Trays
Applications Surface Resistance
106~109 Ω/sq.
Properties Flexural Modulus 10 Millimeter Mm Per Minute
18500 kgf/cm²
Properties Flexural Strength 10 Millimeter Mm Per Minute
310 kgf/cm²
Properties Heat Deflection Temperature 186 Kilogram Kgsq
76 ºC
Properties Izod Impact Notched 32 Millimeter Mm
8 kgf·cm/cm
Properties Melt Flow Index 200 Degree Celsius C Temperat
3.8
Properties Rockwell Hardness L Scale
49
Properties Specific Gravity
1.04
Properties Surface Resistivity At 23 Degree Celsius C Te
5~6 E+Ω/sq
Properties Tensile Elongation At Break 50 Millimeter Mm
70 %
Properties Tensile Strength 50 Millimeter Mm Per Minute
220 kgf/cm²
Properties Test Method For Flexural Modulus 10 Millimete
American Society for Testing and Materials (ASTM) D790
Properties Test Method For Flexural Strength 10 Millimet
American Society for Testing and Materials (ASTM) D790
Properties Test Method For Heat Deflection Temperature 1
American Society for Testing and Materials (ASTM) D648
Properties Test Method For Izod Impact Notched 32 Millim
American Society for Testing and Materials (ASTM) D256
Properties Test Method For Melt Flow Index 200 Degree Ce
American Society for Testing and Materials (ASTM) D1238
Properties Test Method For Rockwell Hardness L Scale
American Society for Testing and Materials (ASTM) D785
Properties Test Method For Specific Gravity
American Society for Testing and Materials (ASTM) D792
Properties Test Method For Surface Resistivity At 23 Deg
American Society for Testing and Materials (ASTM) D257
Properties Test Method For Tensile Elongation At Break 5
American Society for Testing and Materials (ASTM) D638
Properties Test Method For Tensile Strength 50 Millimete
American Society for Testing and Materials (ASTM) D638