Fiberfrax® 1093 Moist Pak-D®, Degree Celsius (ºC) Temperature Grade Blanket
Fiberfrax® 1093 Moist Pak-D®, Degree Celsius (ºC) Temperature Grade Blanket
SKU:FIB-2071db
N/A
Regular price
$49.99
Regular price
Sale price
$49.99
Unit price
per
Initiate Order
Fiberfrax® 1093 Moist Pak-D®, Degree Celsius (ºC) Temperature Grade Blanket
$49.99
Quantity: 1
Claim Your Seller Account
Fiberfrax® 1093 Moist Pak-D®, Degree Celsius (ºC) Temperature Grade Blanket
$49.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
Fiberfrax® Moist Pak-D® insulation is made from high-strength ceramic fiber blankets impregnated with inorganic bonding agents. This processing results in a flexible insulation that air dries to form a hard, rigid structure. Moist Pak-D® is ideal for insulation of complex shapes and for service under conditions of high hot gas velocities.The material is packaged in a clear polyethylene bag to retain the wet binder during shipment and storage. Since damage will occur, care should be taken to prevent freezing of the product.Curing of product can be accomplished by air drying for several days or by immediate exposure to temperature in the application.
Product Specifications
Additional Information
Fibermat® Mat, PH blanket, and Moist Pak-D® insulation provide additional options for specific application requirements ranging from high-temperature filtration to hot gas velocity resistance.Curing is merely a function of removing the water from the inorganic binder.
Note
Normal shelf life one year in unopened containers.Normal shelf life one year in unopened containers.For additional information about product performance or to identify the recommended product for your application, please contact the Unifrax Application Engineering GroupTest data shown are average results of tests conducted under standard procedures and are subject to variation. Results should not be used for specification purposes.
Product Family Characteristics
Excellent handling strengthExcellent hot strengthLow thermal conductivityLow heat storageLight weightResiliencyThermal shock resistanceHigh heat reflectanceExcellent corrosion resistanceExcellent thermal stabilityExcellent sound absorptionExcellent fire protection
Specific Product Characteristics
Exceptional velocity resistanceExcellent conformance to complex shapes
Applications
Hot face layer for Fiberfrax® heater, furnace and kiln linings where hot gas velocities exceed 12.2 m/sec (40 ft/sec)Hot gas duct, flue and stack liningsRecuperator liningsBlow pipe liningsExternal and internal pipe insulationReformer header insulationProcess furnace tube weld protectionThermal and corrosion protection of process heater tube supports
Product Parameters Available Density Dry
190 to 290 kg/m³ | 12 to 18 lb/ft³
Product Parameters Chemical Composition Aluminum Oxide A
23 to 32 %
Product Parameters Chemical Composition Silicon Dioxide
68 to 77 %
Product Parameters Chemical Composition Sodium Carbonate
< 0.5 %
Product Properties Color
White
Product Properties Hot Gas Erosion Resistance
Test procedure based on British Gas Council Research Comm. GC173 = over 30.5 m/sec (100 ft/sec)
Product Properties Mean Fiber Diameter
2 to 3 µm
Product Properties Melting Point
1790 ºC | 3260 ºF
Product Properties Note For Temperature Grade
The temperature grade of Fiberfrax® insulation is determined by irreversible linear change criteria, not product melting point.
Product Properties Recommended Operating Temperature
1850 ºF
Product Properties Specific Heat At 1093 Degree Celsius
1130 J/kg ºC | 0.27 Btu/lb·ºF
Product Properties Temperature Grade
1093 ºC | 2000 ºF
Product Properties Tensile Strength Dry At 64 Millimeter
3.5 x 105 N/m² | 50 psi
Product Properties Tensile Strength Test Method
American Society for Testing and Materials (ASTM 686-76)
Product Properties Tensile Strength Wet At 64 Millimeter
1.2 x 105 N/m² | 17 psi