Griff Polypropylene Release Liner - High Temperature Silicone Coated
Griff Polypropylene Release Liner - High Temperature Silicone Coated
SKU:FIL-8d0d50
Griff Polypropylene Release Liner - High-temp silicone-coated, ideal for mastic compounds.
Regular price
$39.99
Regular price
Sale price
$39.99
Unit price
per
Initiate Order
Griff Polypropylene Release Liner - High Temperature Silicone Coated
$39.99
Quantity: 1
Claim Your Seller Account
Griff Polypropylene Release Liner - High Temperature Silicone Coated
$39.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
Experience superior performance with the Griff Polypropylene Release Liner, specially engineered for high temperature applications and mastic compounds. This release liner, featuring a silicone coating on one side, offers exceptional release properties and durability. With a typical caliper of 1.4 mil and impressive tensile strength, this product ensures reliable performance in demanding environments. Griff's Polypropylene Release Liner provides excellent tear resistance and elongation, meeting the quality standards required for various industrial applications. Trust Griff for unmatched quality and performance.
Product Specifications
Note
The information presented in this data sheet is believed to be accurate and is not intended to constitute a specification. The values given reflect average measurements, which can vary slightly. Users are encouraged to determine the suitability of this product for their own particular application(s).
Specifications Color
Black | Gray
Specifications Material
Polypropylene
Specifications Release Treatment
Silicone One Side
Specifications Type
Release
Terms And Conditions
Seller's only obligation shall be to replace such quantity of the product proven to be defective. Seller shall not be liable for any injury, loss or damage, direct or inconsequential, arising out of the use, or inability to use the product for his/her use, and the user assumes all risk and liability whatsoever in connection therewith. The foregoing may not be changed, except by an agreement signed by an officer or seller. We hereby certify that goods covered by this quotation have been produced in compliance with the Fair Labor Standards Act of 1983, as amended. Any credit memos to purchaser shall expire if not used within one year from date of credit memo.
Testing Parameters
Release test is measured in average grams per inch; 15 minute dwell time, 180° pull at 200 in/min. using Tesa 7475 Tape.
Test Results Test Method For Elongation At Break Md Mach
American Society for Testing and Materials (ASTM) D822A
Test Results Test Method For Elongation At Break Td Tran
American Society for Testing and Materials (ASTM) D822A
Test Results Test Method For Tear Resistance Md Machine
American Society for Testing and Materials (ASTM) D1922
Test Results Test Method For Tear Resistance Td Transver
American Society for Testing and Materials (ASTM) D1922
Test Results Test Method For Tensile Strength Md Machine
American Society for Testing and Materials (ASTM) D822A
Test Results Test Method For Tensile Strength Td Transve
American Society for Testing and Materials (ASTM) D822A
Test Results Caliper
1.4 mil
Test Results Elongation At Break Md Machine Directions
790 %
Test Results Elongation At Break Td Transverse Direction
390 %
Test Results Release Value Gp 1014
5 to 15 g/in
Test Results Tear Resistance Md Machine Directions
15 g
Test Results Tear Resistance Td Transverse Directions
185 g
Test Results Tensile Strength Md Machine Directions
7,220 psi
Test Results Tensile Strength Td Transverse Directions
3,430 psi
Test Results Yield
21,269 lb/in²