    HDT230 High Heat Resin - xPEEK147

    HDT230 High Heat Resin - xPEEK147

    PRO-858012

    Premium xPEEK147 resin for high heat tooling & molding applications, with HDT 230°C & superior mechanical properties.

    $149.99
    $149.99
    Sale

    Initiate Order

    HDT230 High Heat Resin - xPEEK147

    HDT230 High Heat Resin - xPEEK147

    $149.99

    Quantity: 1

    Claim Your Seller Account

    HDT230 High Heat Resin - xPEEK147

    HDT230 High Heat Resin - xPEEK147

    $149.99

    Quantity: 1

    Delivery via Maden

    Expect your order to arrive on time.

    Secure Payments

    All orders are processed through a secure, PCI-compliant checkout.

    View full details
    The xPEEK147 HDT230 High Heat Resin is a premium material designed for high temperature tooling and molding applications, featuring a Heat Deflection Temperature of 230°C. With exceptional dimensional stability, fine surface finish, and superior toughness to endure mechanical stresses, this resin is the ideal choice for projects demanding reliable performance under temperature stress. Developed by renowned brands like Applied Rapid Technologies Corp., Loctite®, and Nexa3D®, this resin delivers outstanding mechanical and thermal properties required for precise tooling applications.

    Product Specifications

    Additional Development Options Additional Development Options
    Colors: xPEEK147 formula can be made in additional pigment colors.Formula Modification for xPEEK147 are possible.
    Liquid Properties Liquid Density
    1.15 g/mL
    Liquid Properties Viscosity At 25 Degree Celsius C 77 Degree Fah
    2105 cP
    Liquid Properties Viscosity Tolerance At 25 Degree Celsius C 77
    200 cP
    Mechanical Properties Green Elongation At Failure
    5.9 %
    Mechanical Properties Green Elongation Tolerance At Failure
    1.7 %
    Mechanical Properties Green Flexural Modulus
    2053 MPa
    Mechanical Properties Green Flexural Modulus Tolerance
    189 MPa
    Mechanical Properties Green Flexural Strain At Break
    7.6 %
    Mechanical Properties Green Flexural Strain At Break Tolerance
    2.7 %
    Mechanical Properties Green Flexural Stress At Yield
    68 MPa
    Mechanical Properties Green Flexural Stress At Yield Tolerance
    3 MPa
    Mechanical Properties Green Tensile Stress At Break
    30.7 MPa
    Mechanical Properties Green Tensile Stress Tolerance At Break
    1.6 MPa
    Mechanical Properties Green Youngs Modulus
    1150 MPa
    Mechanical Properties Green Youngs Modulus Tolerance
    137 MPa
    Mechanical Properties Note For Mechanical Properties
    Based on data provided by Henkel. This information is representative only. Contact your Nexa3D® Technical Service Team for further information.
    Mechanical Properties Post Processed Elongation At Failure
    3.0 %
    Mechanical Properties Post Processed Elongation Tolerance At Fai
    0.1 %
    Mechanical Properties Post Processed Flexural Modulus
    3168 MPa
    Mechanical Properties Post Processed Flexural Modulus Tolerance
    33 MPa
    Mechanical Properties Post Processed Flexural Strain At Break
    4.52 %
    Mechanical Properties Post Processed Flexural Strain At Break To
    0.8 %
    Mechanical Properties Post Processed Flexural Stress At Yield
    128 MPa
    Mechanical Properties Post Processed Flexural Stress At Yield To
    17 MPa
    Mechanical Properties Post Processed Tensile Stress At Break
    75 MPa
    Mechanical Properties Post Processed Tensile Stress Tolerance At
    2 MPa
    Mechanical Properties Post Processed Youngs Modulus
    3192 MPa
    Mechanical Properties Post Processed Youngs Modulus Tolerance
    35 MPa
    Note Note
    All specimen are printed unless otherwise noted. All specimen were conditioned in ambient lab conditions at 19-23C / 40-60 % RH for at least 24 hours."ASTM Methods: D638 Type IV, 5mm/min, D790-B, 2mm/min, D256 Notched IZOD (Machine Notched), 6 mm x 12 mm, D648, D2240, Type "D" (0, 3 seconds), D570 0.125" x 2" Disc 24 hr at 25 ºC, D7867 at 25 ºC (77 ºF), D1475Post cured with Uvitron Intelliray 600 5 min /per side
    Other Properties Green Shrinkage By Density
    8.25 %
    Other Properties Green Solid Density
    1.246 g/cm³
    Other Properties Post Processed Durometer Shore D 0 Sec
    94 Rockwell D
    Other Properties Post Processed Izod Impact Strength
    14.6 J/m
    Other Properties Post Processed Shrinkage By Density
    9.64 %
    Other Properties Post Processed Solid Density
    1.262 g/cm³
    Other Properties Post Processed Water Absorption 24 Hours Hr
    0.25 %
    Post Curing Post Curing
    xPEEK147 requires post curing to achieve specified properties. A wide array of post cure equipment can be used to cure appropriately.
    Specifications Available Colors
    Black | Natural