High-Elongation Black PhotoPlastic Resin
High-Elongation Black PhotoPlastic Resin
SKU:PRO-53a879
Premium high-elongation resin with exceptional impact resistance and surface finish for manufacturing applications.
Regular price
$79.99
Regular price
Sale price
$79.99
Unit price
per
Initiate Order
High-Elongation Black PhotoPlastic Resin
$79.99
Quantity: 1
Claim Your Seller Account
High-Elongation Black PhotoPlastic Resin
$79.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The High-Elongation Black PhotoPlastic Resin xPP405 is a premium material designed for demanding applications requiring exceptional impact resistance, surface finish, and durability. Ideal for manufacturing aids, housings, and consumer goods, this resin offers impressive mechanical properties including high tensile and flexural strength. With post-processing capabilities for superior performance, this resin can be used with various DLP printers, providing a comparable experience to traditional thermoplastics like polypropylene.
Product Specifications
Additional Development Options Additional Development Options
Colors: xPP405-Black formula can be made in additional pigment colors.LCD printers: xPP405-Black currently testing, there's potential.
Limitations Limitations
Vat Printer: xPP405-Black formula is not possible.Post Cure: xPP405-Black requires UV/Visible light post curing.
Liquid Properties Viscosity At 25 Degree Celsius C 77 Degree Fah
2410 cP
Mechanical Properties Green Elongation At Failure
89 %
Mechanical Properties Green Elongation Tolerance At Failure
8 %
Mechanical Properties Green Tensile Stress At Break
24 MPa
Mechanical Properties Green Tensile Stress At Yield
25 MPa
Mechanical Properties Green Tensile Stress Tolerance At Break
1 MPa
Mechanical Properties Green Tensile Stress Tolerance At Yield
1 MPa
Mechanical Properties Green Youngs Modulus
897 MPa
Mechanical Properties Green Youngs Modulus Tolerance
20 MPa
Mechanical Properties Post Processed Elongation At Failure
100 %
Mechanical Properties Post Processed Elongation Tolerance At Fai
12 %
Mechanical Properties Post Processed Flexural Modulus
1300 MPa
Mechanical Properties Post Processed Flexural Modulus Tolerance
65 MPa
Mechanical Properties Post Processed Flexural Strain At Break
Does not Break
Mechanical Properties Post Processed Izod Impact Strength Notche
62 J/m
Mechanical Properties Post Processed Izod Impact Strength Tolera
2 J/m
Mechanical Properties Post Processed Izod Impact Strength Unnotc
> 1500 J/m
Mechanical Properties Post Processed Maximum Flexural Stress
45 MPa
Mechanical Properties Post Processed Maximum Flexural Stress Tol
1 MPa
Mechanical Properties Post Processed Tensile Stress At Break
35 MPa
Mechanical Properties Post Processed Tensile Stress At Yield
38 MPa
Mechanical Properties Post Processed Tensile Stress Tolerance At
1 MPa
Mechanical Properties Post Processed Youngs Modulus
1300 MPa
Mechanical Properties Post Processed Youngs Modulus Tolerance
33 MPa
Note Note
All specimen are printed unless otherwise noted. All specimen were conditioned in ambient lab conditions at 19-23C / 40-60 % RH for at least 24 hours."ASTM Methods: D638 Type IV, 50 mm/min, D790-B, 2 mm/min, D256 Notched IZOD (Machine Notched), 6 mm x 12 mm, D648, D2240, Type "D" (0, 3 seconds), D1475, D7867
Other Properties Green Solid Density
1.116 g/cm³
Other Properties Post Processed Heat Deflection Temperature Hdt
52.8 ºC
Other Properties Post Processed Liquid Density
1.046 g/cm³
Other Properties Post Processed Shore Hardness 0s 3s
80.76 Rockwell D
Other Properties Post Processed Solid Density
1.121 g/cm³
Other Properties Post Processed Water Absorption
1 %
Post Curing Post Curing
xPP405-Black requires post curing to achieve specified properties. A wide array of post cure equipment can be used to cure xPP405-Black appropriately.
Post Processing Post Processing
xPP405-Black requires post processing to achieve specified properties. Prior to post curing, support structures should be removed from the printed part, and the part should be washed in a compatible cleaner. Nexa3D® recommends either IPA or Cleaner C in 2 minute interval wash cycles. Use compressed air to remove residual solvent from the surface of the material between intervals.
Specifications Available Colors
Black