Incoloy® 800HT High Temperature Plate
Incoloy® 800HT High Temperature Plate
SKU:NIC-e88184
Experience superior heat resistance and corrosion protection with the Incoloy® 800HT High Temperature Plate. Ideal for various industrial applications.
Regular price
$2,750.00
Regular price
Sale price
$2,750.00
Unit price
per
Initiate Order
Incoloy® 800HT High Temperature Plate
$2,750.00
Quantity: 1
Claim Your Seller Account
Incoloy® 800HT High Temperature Plate
$2,750.00
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Incoloy® 800HT High Temperature Plate is a premium nickel-iron-chromium alloy renowned for its exceptional strength, oxidation resistance, and longevity in high-temperature settings. Ideal for applications such as process piping, heat exchangers, and nuclear steam-generator tubing, this plate ensures reliable performance under extreme heat conditions. With a composition designed to withstand corrosion and oxidation, it meets stringent industry standards and is a reliable choice for industrial applications requiring durability and heat resistance.
Product Specifications
Nickel Alloy Compositions Alloy
Incoloy 800HT
Nickel Alloy Compositions Astm Specification
ASME SB-409 | ASTM B409 | UNS N08811
Nickel Alloy Compositions Basic Composition
0.015% Max. Sulphur | 0.10% Carbon | 0.60% Aluminum | 0.60% Titanium | 0.75% Max. Copper | 1.0% Max. Silicon | 1.20% Aluminum +Titanium | 1.50% Max. Manganese | 23.0% Chrominum | 35.0% Nickel | 39.5% Min. Iron
Nickel Alloy Compositions Density
0.287 lbs/in³ | 7.94 g/cm³
Specifications Material
Incoloy®
Specifications Plate Weight Per Unit Area
0.51161 lbs/in² | 359.6974381 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
1.750 inches | 44.45 mm
Mechanical Properties Melting Temperature Range
2475 to 2525 ºF | 1357 to 1385 ºC
Mechanical Properties Rupture Strength 1000 H At 1200f65
24000 psi | 165 MPa
Mechanical Properties Rupture Strength 1000 H At 1300f70
15000 psi | 105 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
10000 psi | 70 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
4700 psi | 32 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
2000 psi | 14 MPa