Incoloy 800HT Nickel Alloy Plate
Incoloy 800HT Nickel Alloy Plate
SKU:NIC-7e0fec
Discover the exceptional strength and high-temperature resistance of the Incoloy 800HT Nickel Alloy Plate, perfect for various industrial applications.
Regular price
$189.99
Regular price
Sale price
$189.99
Unit price
per
Initiate Order
Incoloy 800HT Nickel Alloy Plate
$189.99
Quantity: 1
Claim Your Seller Account
Incoloy 800HT Nickel Alloy Plate
$189.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Incoloy 800HT Plate is a high-performance nickel-iron-chromium alloy renowned for its exceptional strength, resistance to oxidation, and durability in high-temperature environments. Perfect for process piping, heat exchangers, carburizing equipment, and more, this plate maintains stability even under prolonged heat exposure. With a composition that includes 35.0% Nickel, 23.0% Chromium, and complying with ASTM specifications ASME SB-409, ASTM B409, and UNS N08811, this plate offers superior performance and reliability for industrial applications.
Ready to Grow Without Cash Flow Constraints?
Product Specifications
Nickel Alloy Compositions Alloy
Incoloy 800HT
Nickel Alloy Compositions Astm Specification
ASME SB-409 | ASTM B409 | UNS N08811
Nickel Alloy Compositions Basic Composition
0.015% Max. Sulphur | 0.10% Carbon | 0.60% Aluminum | 0.60% Titanium | 0.75% Max. Copper | 1.0% Max. Silicon | 1.20% Aluminum +Titanium | 1.50% Max. Manganese | 23.0% Chrominum | 35.0% Nickel | 39.5% Min. Iron
Nickel Alloy Compositions Density
0.287 lbs/in³ | 7.94 g/cm³
Specifications Material
Incoloy®
Specifications Plate Weight Per Unit Area
0.36806 lbs/in² | 258.771797 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
1.250 inches | 31.75 mm
Mechanical Properties Melting Temperature Range
2475 to 2525 ºF | 1357 to 1385 ºC
Mechanical Properties Rupture Strength 1000 H At 1200f65
24000 psi | 165 MPa
Mechanical Properties Rupture Strength 1000 H At 1300f70
15000 psi | 105 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
10000 psi | 70 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
4700 psi | 32 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
2000 psi | 14 MPa