Incoloy 800HT Plate - High-Temperature Nickel Alloy
Incoloy 800HT Plate - High-Temperature Nickel Alloy
SKU:NIC-24bc9f
Explore the Incoloy 800HT Plate - A high-performance solution for extreme heat applications.
Regular price
$2,500.00
Regular price
Sale price
$2,500.00
Unit price
per
Initiate Order
Incoloy 800HT Plate - High-Temperature Nickel Alloy
$2,500.00
Quantity: 1
Claim Your Seller Account
Incoloy 800HT Plate - High-Temperature Nickel Alloy
$2,500.00
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Incoloy 800HT Plate is a premium nickel-iron-chromium alloy renowned for its exceptional strength and resistance to oxidation, carburization, and corrosion in high-temperature environments. Crafted to maintain structural integrity under prolonged heat exposure, this plate is ideal for critical applications like process piping, heat exchangers, carburizing equipment, and more. With ASTM specifications including ASME SB-409, ASTM B409, and UNS N08811, this plate offers reliability and performance in demanding industrial settings.
Product Specifications
Nickel Alloy Compositions Alloy
Incoloy 800HT
Nickel Alloy Compositions Astm Specification
ASME SB-409 | ASTM B409 | UNS N08811
Nickel Alloy Compositions Basic Composition
0.015% Max. Sulphur | 0.10% Carbon | 0.60% Aluminum | 0.60% Titanium | 0.75% Max. Copper | 1.0% Max. Silicon | 1.20% Aluminum +Titanium | 1.50% Max. Manganese | 23.0% Chrominum | 35.0% Nickel | 39.5% Min. Iron
Nickel Alloy Compositions Density
0.287 lbs/in³ | 7.94 g/cm³
Specifications Material
Incoloy®
Specifications Plate Weight Per Unit Area
0.87709 lbs/in² | 616.6553155 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
3.000 inches | 76.2 mm
Mechanical Properties Melting Temperature Range
2475 to 2525 ºF | 1357 to 1385 ºC
Mechanical Properties Rupture Strength 1000 H At 1200f65
24000 psi | 165 MPa
Mechanical Properties Rupture Strength 1000 H At 1300f70
15000 psi | 105 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
10000 psi | 70 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
4700 psi | 32 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
2000 psi | 14 MPa