Incoloy® 800HT High-Temperature Plate
Incoloy® 800HT High-Temperature Plate
SKU:NIC-7d646c
Top-tier nickel-iron-chromium alloy plate, renowned for exceptional strength and high-temperature durability in critical applications.
Regular price
$2,499.99
Regular price
Sale price
$2,499.99
Unit price
per
Initiate Order
Incoloy® 800HT High-Temperature Plate
$2,499.99
Quantity: 1
Claim Your Seller Account
Incoloy® 800HT High-Temperature Plate
$2,499.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Incoloy® 800HT Plate is a top-tier nickel-iron-chromium alloy renowned for its robust strength, exceptional resistance to oxidation, and longevity in high-temperature settings. Designed to withstand demanding conditions, it excels in applications like process piping, heat exchangers, and nuclear steam-generator tubing. With properties like stable austenitic structure retention at elevated temperatures, this plate ensures reliability and longevity in critical operations.
Product Specifications
Nickel Alloy Compositions Alloy
Incoloy 800HT
Nickel Alloy Compositions Astm Specification
ASME SB-409 | ASTM B409 | UNS N08811
Nickel Alloy Compositions Basic Composition
0.015% Max. Sulphur | 0.10% Carbon | 0.60% Aluminum | 0.60% Titanium | 0.75% Max. Copper | 1.0% Max. Silicon | 1.20% Aluminum +Titanium | 1.50% Max. Manganese | 23.0% Chrominum | 35.0% Nickel | 39.5% Min. Iron
Nickel Alloy Compositions Density
0.287 lbs/in³ | 7.94 g/cm³
Specifications Material
Incoloy®
Specifications Plate Weight Per Unit Area
0.09700 lbs/in² | 68.1977512 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
0.3125 inches | 7.92 mm
Mechanical Properties Melting Temperature Range
2475 to 2525 ºF | 1357 to 1385 ºC
Mechanical Properties Rupture Strength 1000 H At 1200f65
24000 psi | 165 MPa
Mechanical Properties Rupture Strength 1000 H At 1300f70
15000 psi | 105 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
10000 psi | 70 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
4700 psi | 32 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
2000 psi | 14 MPa