Incoloy® 800HT Nickel Alloy Sheet
Incoloy® 800HT Nickel Alloy Sheet
SKU:NIC-cfcaff
High-performance Incoloy® 800HT Sheet with exceptional strength, resistance to oxidation, and stability in high temperatures. Ideal for various industrial applications.
Regular price
$45.99
Regular price
Sale price
$45.99
Unit price
per
Initiate Order
Incoloy® 800HT Nickel Alloy Sheet
$45.99
Quantity: 1
Claim Your Seller Account
Incoloy® 800HT Nickel Alloy Sheet
$45.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Incoloy® 800HT Sheet is a high-performance nickel-iron-chromium alloy designed for extreme high-temperature environments. With exceptional strength, superior resistance to oxidation, carburization, and corrosion, this sheet maintains its stability even under prolonged exposure to heat. Ideal for various applications including process piping, heat exchangers, carburizing equipment, and more. Manufactured to meet ASME SB-409, ASTM B409, and UNS N08811 standards.
Product Specifications
Nickel Alloy Compositions Alloy
Incoloy 800HT
Nickel Alloy Compositions Astm Specification
ASME SB-409 | ASTM B409 | UNS N08811
Nickel Alloy Compositions Basic Composition
0.015% Max. Sulphur | 0.10% Carbon | 0.60% Aluminum | 0.60% Titanium | 0.75% Max. Copper | 1.0% Max. Silicon | 1.20% Aluminum +Titanium | 1.50% Max. Manganese | 23.0% Chrominum | 35.0% Nickel | 39.5% Min. Iron
Nickel Alloy Compositions Density
0.287 lbs/in³ | 7.94 g/cm³
Specifications Material
Incoloy®
Specifications Shapeform
Sheets
Specifications Thickness
0.025 inches | 0.6350 mm
Mechanical Properties Melting Temperature Range
2475 to 2525 ºF | 1357 to 1385 ºC
Mechanical Properties Rupture Strength 1000 H At 1200f65
24000 psi | 165 MPa
Mechanical Properties Rupture Strength 1000 H At 1300f70
15000 psi | 105 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
10000 psi | 70 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
4700 psi | 32 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
2000 psi | 14 MPa