Incoloy® 800HT Nickel Alloy Sheet
Incoloy® 800HT Nickel Alloy Sheet
SKU:NIC-c93f61
Explore the Incoloy® 800HT Nickel Alloy Sheet for unparalleled high-temperature resistance and corrosion protection. Ideal for critical applications.
Regular price
$129.99
Regular price
Sale price
$129.99
Unit price
per
Initiate Order
Incoloy® 800HT Nickel Alloy Sheet
$129.99
Quantity: 1
Claim Your Seller Account
Incoloy® 800HT Nickel Alloy Sheet
$129.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Incoloy® 800HT Nickel Alloy Sheet is a high-performance material known for its exceptional strength, resistance to oxidation, and superior corrosion resistance in high-temperature environments. This alloy maintains stability even under prolonged exposure to extreme heat, making it ideal for critical applications like process piping, heat exchangers, and nuclear steam-generator tubing. With a composition featuring nickel, iron, chromium, aluminum, titanium, and other elements, this sheet ensures reliable performance in demanding industrial settings.
Product Specifications
Nickel Alloy Compositions Alloy
Incoloy 800HT
Nickel Alloy Compositions Astm Specification
ASME SB-409 | ASTM B409 | UNS N08811
Nickel Alloy Compositions Basic Composition
0.015% Max. Sulphur | 0.10% Carbon | 0.60% Aluminum | 0.60% Titanium | 0.75% Max. Copper | 1.0% Max. Silicon | 1.20% Aluminum +Titanium | 1.50% Max. Manganese | 23.0% Chrominum | 35.0% Nickel | 39.5% Min. Iron
Nickel Alloy Compositions Density
0.287 lbs/in³ | 7.94 g/cm³
Specifications Material
Incoloy®
Specifications Shapeform
Sheets
Specifications Thickness
0.093 inches | 2.3622 mm
Mechanical Properties Melting Temperature Range
2475 to 2525 ºF | 1357 to 1385 ºC
Mechanical Properties Rupture Strength 1000 H At 1200f65
24000 psi | 165 MPa
Mechanical Properties Rupture Strength 1000 H At 1300f70
15000 psi | 105 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
10000 psi | 70 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
4700 psi | 32 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
2000 psi | 14 MPa