Inconel 330 High Temperature Alloy Plate
Inconel 330 High Temperature Alloy Plate
SKU:NIC-a5cb44
Inconel 330 Plate - High-temperature strength, exceptional oxidation resistance, and superior durability for industrial heating applications.
Regular price
$349.99
Regular price
Sale price
$349.99
Unit price
per
Initiate Order
Inconel 330 High Temperature Alloy Plate
$349.99
Quantity: 1
Claim Your Seller Account
Inconel 330 High Temperature Alloy Plate
$349.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Inconel 330 Plate is a superior nickel-iron-chromium alloy infused with silicon, designed for exceptional oxidation resistance, high-temperature strength, and unmatched durability. Its austenitic microstructure ensures stability during prolonged exposure to extreme heat, making it ideal for industrial applications like furnace muffles, retorts, and heat-treating fixtures. With a thickness of 1.750 inches and a composition of 1.1% Silicon, 18.5% Chromium, 35.5% Nickel, and 44.0% Iron, this plate offers unrivaled performance in harsh carburizing and oxidizing environments. Meet your demanding high-temperature needs with the reliability of Inconel 330 Plate.
Product Specifications
Nickel Alloy Compositions Alloy
Incoloy 330
Nickel Alloy Compositions Astm Specification
ASME SB-536 | ASTM B-536 | SAE 5592 | UNS N08330
Nickel Alloy Compositions Basic Composition
1.1% Silicon | 18.5% Chrominum | 35.5% Nickel | 44.0% Iron
Nickel Alloy Compositions Density
0.292 lbs/in³ | 8.08 g/cm³
Specifications Material
Incoloy®
Specifications Plate Weight Per Unit Area
0.51161 lbs/in² | 359.697438056 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
1.750 inches | 44.45 mm
Mechanical Properties Melting Temperature Range
2450 to 2600 ºF | 1345 to 1425 ºC
Mechanical Properties Rupture Strength 1000 H At 1400f76
7000 psi | 48 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
3100 psi | 21 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
1250 psi | 8.6 MPa
Mechanical Properties Rupture Strength 1000 H At 2000f10
780 psi | 5.4 MPa