Premium nickel-iron-chromium alloy plate with exceptional oxidation resistance and high-temperature strength. Ideal for industrial heating applications.
Regular price
$250.00
Regular price
Sale price
$250.00
Unit price
per
Initiate Order
Inconel 330 Plate - High Temperature Alloy
$250.00
Quantity: 1
Claim Your Seller Account
Inconel 330 Plate - High Temperature Alloy
$250.00
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Inconel 330 Plate is a premium nickel-iron-chromium alloy designed with enhanced silicon for superior oxidation resistance. With exceptional strength at high temperatures and excellent resistance to carburizing and oxidizing environments, this alloy maintains a stable austenitic microstructure over prolonged high-temperature exposures. Ideal for industrial heating applications such as furnace muffles, retorts, conveyor systems, heat-treating baskets, and fixtures, this plate in 1.250-inch thickness offers reliability and durability in demanding environments.
Product Specifications
Nickel Alloy Compositions Alloy
Incoloy 330
Nickel Alloy Compositions Astm Specification
ASME SB-536 | ASTM B-536 | SAE 5592 | UNS N08330
Nickel Alloy Compositions Basic Composition
1.1% Silicon | 18.5% Chrominum | 35.5% Nickel | 44.0% Iron
Nickel Alloy Compositions Density
0.292 lbs/in³ | 8.08 g/cm³
Specifications Material
Incoloy®
Specifications Plate Weight Per Unit Area
0.36806 lbs/in² | 258.771796976 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
1.250 inches | 31.75 mm
Mechanical Properties Melting Temperature Range
2450 to 2600 ºF | 1345 to 1425 ºC
Mechanical Properties Rupture Strength 1000 H At 1400f76
7000 psi | 48 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
3100 psi | 21 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
1250 psi | 8.6 MPa
Mechanical Properties Rupture Strength 1000 H At 2000f10
780 psi | 5.4 MPa