Inconel 330 Plate - High Temperature Nickel Alloy
Inconel 330 Plate - High Temperature Nickel Alloy
SKU:NIC-4a6889
High-quality Inconel 330 Plate offering exceptional oxidation resistance and high-temperature strength. Ideal for industrial heating applications.
Regular price
$350.00
Regular price
Sale price
$350.00
Unit price
per
Initiate Order
Inconel 330 Plate - High Temperature Nickel Alloy
$350.00
Quantity: 1
Claim Your Seller Account
Inconel 330 Plate - High Temperature Nickel Alloy
$350.00
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Inconel® 330 Plate is a premium nickel-iron-chromium alloy featuring added silicon for superior oxidation resistance. Its robust strength at high temperatures, along with exceptional resistance to carburizing and oxidizing environments, makes it ideal for industrial heating applications. This alloy's stable austenitic microstructure ensures dependable performance even during prolonged exposure to extreme heat. Commonly used in furnace muffles, retorts, conveyor systems, heat-treating baskets, and fixtures. Compliant with ASTM specifications ASME SB-536, ASTM B-536, SAE 5592, and UNS N08330.
Product Specifications
Nickel Alloy Compositions Alloy
Incoloy 330
Nickel Alloy Compositions Astm Specification
ASME SB-536 | ASTM B-536 | SAE 5592 | UNS N08330
Nickel Alloy Compositions Basic Composition
1.1% Silicon | 18.5% Chrominum | 35.5% Nickel | 44.0% Iron
Nickel Alloy Compositions Density
0.292 lbs/in³ | 8.08 g/cm³
Specifications Material
Incoloy®
Specifications Plate Weight Per Unit Area
0.43984 lbs/in² | 309.238132864 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
1.500 inches | 38.1 mm
Mechanical Properties Melting Temperature Range
2450 to 2600 ºF | 1345 to 1425 ºC
Mechanical Properties Rupture Strength 1000 H At 1400f76
7000 psi | 48 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
3100 psi | 21 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
1250 psi | 8.6 MPa
Mechanical Properties Rupture Strength 1000 H At 2000f10
780 psi | 5.4 MPa