Inconel 601 High-Temperature Alloy Plate
Inconel 601 High-Temperature Alloy Plate
SKU:NIC-c676d9
Premium Inconel 601 Plate for high-temp applications, unmatched oxidation resistance & mechanical strength. ASTM compliant.
Regular price
$199.99
Regular price
Sale price
$199.99
Unit price
per
Initiate Order
Inconel 601 High-Temperature Alloy Plate
$199.99
Quantity: 1
Claim Your Seller Account
Inconel 601 High-Temperature Alloy Plate
$199.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Inconel® 601 Plate is a premium nickel-chromium alloy with added aluminum, delivering exceptional resistance to oxidation and high-temperature corrosion. With superior mechanical properties at elevated temperatures, this plate is ideal for industrial furnaces, heat-treating equipment, petrochemical processes, and gas-turbine components. Compliant with stringent ASTM specifications including ASME SB-168 and ASTM B168, this plate is available in a thickness of 0.25 inches (6.35 mm), offering durability and reliability in demanding environments.
Product Specifications
Nickel Alloy Compositions Alloy
Inconel® 601
Nickel Alloy Compositions Astm Specification
ASME SB-168 | ASTM B168 | SAE 5870 | UNS N06601
Nickel Alloy Compositions Basic Composition
1.4% Aluminum | 14.4% Iron | 23.0% Chrominum | 60.5% Nickel
Nickel Alloy Compositions Density
0.291 lbs/in³ | 8.06 g/cm³
Specifications Material
Inconel®
Specifications Plate Weight Per Unit Area
0.0795 lbs/in² | 55.8940332 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
0.25 inches | 6.3500 mm
Mechanical Properties Melting Temperature Range
2480 to 2571 ºF | 1360 to 1411 ºC
Mechanical Properties Rupture Strength 1000 H At 1200f65
28000 psi | 195 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
9100 psi | 63 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
4300 psi | 30 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
2100 psi | 14 MPa
Mechanical Properties Rupture Strength 1000 H At 2000f10
1000 psi | 7 MPa