Inconel 617 High Temp Plate 1.750" Thick
Inconel 617 High Temp Plate 1.750" Thick
SKU:NIC-6252b8
High-quality Inconel 617 Plate: Exceptional strength and oxidation resistance for high-temp applications. Meets ASTM standards.
Regular price
$1,450.00
Regular price
Sale price
$1,450.00
Unit price
per
Initiate Order
Inconel 617 High Temp Plate 1.750" Thick
$1,450.00
Quantity: 1
Claim Your Seller Account
Inconel 617 High Temp Plate 1.750" Thick
$1,450.00
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Inconel 617 Plate is a top-notch nickel-chromium-cobalt-molybdenum alloy renowned for its exceptional metallurgical stability, strength, and oxidation resistance at high temperatures. With enhanced resistance to oxidation from aluminum, this plate is ideal for demanding applications like gas turbines, petrochemical processing, and heat-treating equipment. Its composition, including 52.0% Nickel, 22.0% Chromium, and 9.0% Molybdenum, ensures durable performance. This product meets ASTM standards ASME SB-166(w) and ASTM B166(w) and is suitable for various industries requiring high-temperature stability.
Product Specifications
Nickel Alloy Compositions Alloy
Inconel® 617
Nickel Alloy Compositions Astm Specification
ASME SB-166(w) | ASTM B166(w) | SAE 5887 | UNS N06617
Nickel Alloy Compositions Basic Composition
1.2% Aluminum | 1.5% Iron | 125% Cobalt | 22.0% Chrominum | 52.0% Nickel | 9.0% Molybdenum
Nickel Alloy Compositions Density
0.302 lbs/in³ | 8.36 g/cm³
Specifications Material
Inconel®
Specifications Plate Weight Per Unit Area
0.55526 lbs/in² | 390.386426096 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
1.750 inches | 44.45 mm
Mechanical Properties Melting Temperature Range
2430 to 2510 ºF | 1330 to 1380 ºC
Mechanical Properties Rupture Strength 1000 H At 1200f65
47000 psi | 320 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
22000 psi | 150 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
8400 psi | 58 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
3600 psi | 25 MPa
Mechanical Properties Rupture Strength 1000 H At 2000f10
1500 psi | 10 MPa