Inconel 617 High Temperature Alloy Plate
Inconel 617 High Temperature Alloy Plate
SKU:NIC-8bda41
Discover the Inconel 617 Plate: a high-strength, oxidation-resistant nickel alloy plate for extreme temperature operations.
Regular price
$1,200.00
Regular price
Sale price
$1,200.00
Unit price
per
Initiate Order
Inconel 617 High Temperature Alloy Plate
$1,200.00
Quantity: 1
Claim Your Seller Account
Inconel 617 High Temperature Alloy Plate
$1,200.00
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Inconel 617 Plate is a cutting-edge nickel-chromium-cobalt-molybdenum alloy renowned for its exceptional metallurgical stability, strength, and oxidation resistance, making it ideal for high-temperature applications. With added aluminum for enhanced oxidation resistance, this plate also exhibits outstanding resistance to corrosive aqueous environments. Commonly used in gas turbines, petrochemical processing, heat-treating equipment, and nitric acid production, the Inconel 617 Plate is available in various forms including plates, sheets, and tubes, meeting stringent industry standards.
Product Specifications
Nickel Alloy Compositions Alloy
Inconel® 617
Nickel Alloy Compositions Astm Specification
ASME SB-166(w) | ASTM B166(w) | SAE 5887 | UNS N06617
Nickel Alloy Compositions Basic Composition
1.2% Aluminum | 1.5% Iron | 125% Cobalt | 22.0% Chrominum | 52.0% Nickel | 9.0% Molybdenum
Nickel Alloy Compositions Density
0.302 lbs/in³ | 8.36 g/cm³
Specifications Material
Inconel®
Specifications Plate Weight Per Unit Area
0.87255 lbs/in² | 613.46337948 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
2.75 inches | 69.85 mm
Mechanical Properties Melting Temperature Range
2430 to 2510 ºF | 1330 to 1380 ºC
Mechanical Properties Rupture Strength 1000 H At 1200f65
47000 psi | 320 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
22000 psi | 150 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
8400 psi | 58 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
3600 psi | 25 MPa
Mechanical Properties Rupture Strength 1000 H At 2000f10
1500 psi | 10 MPa