Inconel 617 Plate for High-Temperature Applications
Inconel 617 Plate for High-Temperature Applications
SKU:NIC-18787d
Premium Inconel 617 Plate for high-temp applications. Exceptional strength and oxidation resistance. Meets ASTM standards.
Regular price
$2,000.00
Regular price
Sale price
$2,000.00
Unit price
per
Initiate Order
Inconel 617 Plate for High-Temperature Applications
$2,000.00
Quantity: 1
Claim Your Seller Account
Inconel 617 Plate for High-Temperature Applications
$2,000.00
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Inconel 617 Plate is a premium nickel-chromium-cobalt-molybdenum alloy renowned for its exceptional metallurgical stability, high strength, and superb oxidation resistance, making it ideal for demanding high-temperature environments. With added aluminum for enhanced oxidation resistance, this plate is a top choice for gas turbines, petrochemical processing, heat-treating equipment, and nitric acid production. Manufactured to meet ASTM specifications such as ASME SB-166(w) and ASTM B166(w), this plate offers reliable performance and durability in corrosive aqueous environments.
Product Specifications
Nickel Alloy Compositions Alloy
Inconel® 617
Nickel Alloy Compositions Astm Specification
ASME SB-166(w) | ASTM B166(w) | SAE 5887 | UNS N06617
Nickel Alloy Compositions Basic Composition
1.2% Aluminum | 1.5% Iron | 125% Cobalt | 22.0% Chrominum | 52.0% Nickel | 9.0% Molybdenum
Nickel Alloy Compositions Density
0.302 lbs/in³ | 8.36 g/cm³
Specifications Material
Inconel®
Specifications Plate Weight Per Unit Area
0.95188 lbs/in² | 669.237890848 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
3.000 inches | 76.2 mm
Mechanical Properties Melting Temperature Range
2430 to 2510 ºF | 1330 to 1380 ºC
Mechanical Properties Rupture Strength 1000 H At 1200f65
47000 psi | 320 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
22000 psi | 150 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
8400 psi | 58 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
3600 psi | 25 MPa
Mechanical Properties Rupture Strength 1000 H At 2000f10
1500 psi | 10 MPa