Inconel 625 High-Strength Nickel Alloy Plate
Inconel 625 High-Strength Nickel Alloy Plate
SKU:NIC-6a29f2
High-strength Inconel 625 Plate for demanding environments. Resistant to corrosion and crevice corrosion, with superior strength characteristics.
Regular price
$399.99
Regular price
Sale price
$399.99
Unit price
per
Initiate Order
Inconel 625 High-Strength Nickel Alloy Plate
$399.99
Quantity: 1
Claim Your Seller Account
Inconel 625 High-Strength Nickel Alloy Plate
$399.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Inconel 625 Plate is a high-performance nickel-chromium-molybdenum alloy featuring niobium addition for exceptional strength without heat treatment. Ideal for demanding environments, it resists corrosion, pitting, and crevice corrosion. With a thickness of 3.000 inches and a weight of 0.941 lbs/in², this plate meets ASTM specifications including ASME SB-443, ASTM B-443, and more. From aerospace to nuclear reactors, this plate excels in chemical processing, marine engineering, and pollution control.
Ready to Grow Without Cash Flow Constraints?
Product Specifications
Nickel Alloy Compositions Alloy
Inconel® 625
Nickel Alloy Compositions Astm Specification
ASME SB-443 | ASTM B-443 | SAE 5599 | SAE 5869 | UNS N06625
Nickel Alloy Compositions Basic Composition
1.0% Iron | 16.3% Molybdenum | 20.5% Chrominum | 3.8% Tungsten | 58.0% Nickel
Nickel Alloy Compositions Density
0.315 lbs/in³ | 8.72 g/cm³
Specifications Material
Inconel®
Specifications Plate Weight Per Unit Area
0.941 lbs/in² | 661.5884936 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
3.000 inches | 76.2 mm
Mechanical Properties Melting Temperature Range
2350 to 2460 ºF | 1290 to 1350 ºC
Mechanical Properties Rupture Strength 1000 H At 1200f65
52000 psi | 360 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
23000 psi | 160 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
7200 psi | 50 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
2600 psi | 18 MPa