Inconel 718 Plate - High Strength Nickel Alloy
Inconel 718 Plate - High Strength Nickel Alloy
SKU:NIC-4d6b55
High-strength Inconel 718 Plate with exceptional corrosion resistance and weldability. Ideal for gas turbines, rocket motors, spacecraft, and more.
Regular price
$1,500.00
Regular price
Sale price
$1,500.00
Unit price
per
Initiate Order
Inconel 718 Plate - High Strength Nickel Alloy
$1,500.00
Quantity: 1
Claim Your Seller Account
Inconel 718 Plate - High Strength Nickel Alloy
$1,500.00
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Inconel 718 Plate is a precipitation-hardenable alloy known for its corrosion resistance, exceptional weldability, and high strength properties, making it ideal for demanding applications in gas turbines, rocket motors, spacecraft, nuclear reactors, pumps, and tooling. With a melting temperature range of 2300 to 2437°F, it offers excellent creep-rupture strength up to 1300°F. This ASTM B670, SAE 5597, UNS N07718 compliant plate is composed of 18% Chromium, 18.5% Iron, 3% Molybdenum, 5% Niobium, and 54% Nickel, ensuring premium quality and durability.
Product Specifications
Nickel Alloy Compositions Alloy
Inconel® 718
Nickel Alloy Compositions Astm Specification
ASTM B670 | SAE 5597 | UNS N07718
Nickel Alloy Compositions Basic Composition
18.0% Chrominum | 18.5% Iron | 3.0% Molybdenum | 5.0% Niobium | 54.0% Nickel
Nickel Alloy Compositions Density
0.296 lbs/in³ | 8.19 g/cm³
Specifications Material
Inconel®
Specifications Plate Weight Per Unit Area
0.392 lbs/in² | 275.6032832 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
1.250 inches | 31.75 mm
Mechanical Properties Melting Temperature Range
2300 to 2437 ºF | 1260 to 1336 ºC
Mechanical Properties Rupture Strength 1000 H At 1100f59
110000 psi | 760 MPa
Mechanical Properties Rupture Strength 1000 H At 1200f65
86000 psi | 590 MPa
Mechanical Properties Rupture Strength 1000 H At 1300f70
53000 psi | 370 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
24000 psi | 170 MPa