Inconel® 617 High-Temperature Alloy Plate
Inconel® 617 High-Temperature Alloy Plate
SKU:NIC-885cab
Unmatched metallurgical stability and oxidation resistance in the Inconel® 617 Plate. Ideal for high-temp environments like gas turbines.
Regular price
$299.99
Regular price
Sale price
$299.99
Unit price
per
Initiate Order
Inconel® 617 High-Temperature Alloy Plate
$299.99
Quantity: 1
Claim Your Seller Account
Inconel® 617 High-Temperature Alloy Plate
$299.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
Experience unmatched metallurgical stability, strength, and oxidation resistance with the Inconel® 617 Plate. This nickel-chromium-cobalt-molybdenum alloy features exceptional resistance to oxidation, making it ideal for gas turbines, petrochemical processing, and heat-treating equipment. With a thickness of 2.250 inches and ASTM specifications including ASME SB-166(w) and ASTM B166(w), this plate offers reliable performance at extreme temperatures. Rupture strength data at various temperatures further underscores its durability and suitability for demanding applications.
Product Specifications
Nickel Alloy Compositions Alloy
Inconel® 617
Nickel Alloy Compositions Astm Specification
ASME SB-166(w) | ASTM B166(w) | SAE 5887 | UNS N06617
Nickel Alloy Compositions Basic Composition
1.2% Aluminum | 1.5% Iron | 125% Cobalt | 22.0% Chrominum | 52.0% Nickel | 9.0% Molybdenum
Nickel Alloy Compositions Density
0.302 lbs/in³ | 8.36 g/cm³
Specifications Material
Inconel®
Specifications Plate Weight Per Unit Area
0.71391 lbs/in² | 501.928418136 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
2.250 inches | 57.15 mm
Mechanical Properties Melting Temperature Range
2430 to 2510 ºF | 1330 to 1380 ºC
Mechanical Properties Rupture Strength 1000 H At 1200f65
47000 psi | 320 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
22000 psi | 150 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
8400 psi | 58 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
3600 psi | 25 MPa
Mechanical Properties Rupture Strength 1000 H At 2000f10
1500 psi | 10 MPa