Inconel® 617 High-Temperature Plate
Inconel® 617 High-Temperature Plate
SKU:NIC-ebb8ad
Explore the Inconel® 617 Plate, a high-performance nickel alloy designed for stability, strength, and oxidation resistance at extreme temperatures.
Regular price
$2,500.00
Regular price
Sale price
$2,500.00
Unit price
per
Initiate Order
Inconel® 617 High-Temperature Plate
$2,500.00
Quantity: 1
Claim Your Seller Account
Inconel® 617 High-Temperature Plate
$2,500.00
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Inconel® 617 Plate is a premier nickel-chromium-cobalt-molybdenum alloy renowned for its exceptional metallurgical stability, strength, and oxidation resistance at elevated temperatures. With added aluminum for enhanced oxidation resistance, this plate resists corrosive aqueous environments. Ideal for applications in gas turbines, petrochemical processing, heat-treating equipment, and nitric acid production. This product conforms to ASME SB-166(w), ASTM B166(w), SAE 5887, and UNS N06617 standards.
Product Specifications
Nickel Alloy Compositions Alloy
Inconel® 617
Nickel Alloy Compositions Astm Specification
ASME SB-166(w) | ASTM B166(w) | SAE 5887 | UNS N06617
Nickel Alloy Compositions Basic Composition
1.2% Aluminum | 1.5% Iron | 125% Cobalt | 22.0% Chrominum | 52.0% Nickel | 9.0% Molybdenum
Nickel Alloy Compositions Density
0.302 lbs/in³ | 8.36 g/cm³
Specifications Material
Inconel®
Specifications Plate Weight Per Unit Area
0.28032 lbs/in² | 197.084470272 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
0.875 inches | 22.22 mm
Mechanical Properties Melting Temperature Range
2430 to 2510 ºF | 1330 to 1380 ºC
Mechanical Properties Rupture Strength 1000 H At 1200f65
47000 psi | 320 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
22000 psi | 150 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
8400 psi | 58 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
3600 psi | 25 MPa
Mechanical Properties Rupture Strength 1000 H At 2000f10
1500 psi | 10 MPa