Inconel® 617 High Temperature Plate - 0.625 inches
Inconel® 617 High Temperature Plate - 0.625 inches
SKU:NIC-9860f1
Discover the superior quality of Inconel® 617 Plate - perfect for high-temperature applications.
Regular price
$250.00
Regular price
Sale price
$250.00
Unit price
per
Initiate Order
Inconel® 617 High Temperature Plate - 0.625 inches
$250.00
Quantity: 1
Claim Your Seller Account
Inconel® 617 High Temperature Plate - 0.625 inches
$250.00
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Inconel® 617 Plate is a top-of-the-line nickel-chromium-cobalt-molybdenum alloy known for its exceptional metallurgical stability, strength, and oxidation resistance even at high temperatures. With added aluminum for enhanced oxidation resistance, this plate also stands strong against a wide range of corrosive aqueous environments. Ideal for gas turbines, petrochemical processing, heat-treating equipment, and nitric acid production, this plate comes in a thickness of 0.625 inches, meeting stringent industry standards like ASTM B166 and UNS N06617.
Product Specifications
Nickel Alloy Compositions Alloy
Inconel® 617
Nickel Alloy Compositions Astm Specification
ASME SB-166(w) | ASTM B166(w) | SAE 5887 | UNS N06617
Nickel Alloy Compositions Basic Composition
1.2% Aluminum | 1.5% Iron | 125% Cobalt | 22.0% Chrominum | 52.0% Nickel | 9.0% Molybdenum
Nickel Alloy Compositions Density
0.302 lbs/in³ | 8.36 g/cm³
Specifications Material
Inconel®
Specifications Plate Weight Per Unit Area
0.20023 lbs/in² | 140.775626008 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
0.625 inches | 15.87 mm
Mechanical Properties Melting Temperature Range
2430 to 2510 ºF | 1330 to 1380 ºC
Mechanical Properties Rupture Strength 1000 H At 1200f65
47000 psi | 320 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
22000 psi | 150 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
8400 psi | 58 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
3600 psi | 25 MPa
Mechanical Properties Rupture Strength 1000 H At 2000f10
1500 psi | 10 MPa