Inconel® 625 Plate - High Strength Nickel Alloy
Inconel® 625 Plate - High Strength Nickel Alloy
SKU:NIC-32fb31
Explore the high-strength capabilities of Inconel® 625 Plate. Ideal for corrosive environments in aerospace, chemical, and nuclear applications.
Regular price
$350.00
Regular price
Sale price
$350.00
Unit price
per
Initiate Order
Inconel® 625 Plate - High Strength Nickel Alloy
$350.00
Quantity: 1
Claim Your Seller Account
Inconel® 625 Plate - High Strength Nickel Alloy
$350.00
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Inconel® 625 Plate is a premium nickel-chromium-molybdenum alloy crafted with niobium for exceptional matrix stiffening, offering unparalleled strength without the need for heat treatment. Resistant to a wide array of corrosive environments, it excels in chemical processing, aerospace, marine engineering, pollution-control, and nuclear applications. With precise specifications meeting ASTM standards, this plate delivers reliability and longevity in demanding industrial settings.
Ready to Grow Without Cash Flow Constraints?
Product Specifications
Nickel Alloy Compositions Alloy
Inconel® 625
Nickel Alloy Compositions Astm Specification
ASME SB-443 | ASTM B-443 | SAE 5599 | SAE 5869 | UNS N06625
Nickel Alloy Compositions Basic Composition
1.0% Iron | 16.3% Molybdenum | 20.5% Chrominum | 3.8% Tungsten | 58.0% Nickel
Nickel Alloy Compositions Density
0.315 lbs/in³ | 8.72 g/cm³
Specifications Material
Inconel®
Specifications Plate Weight Per Unit Area
0.06000 lbs/in² | 42.184176 kg/m²
Specifications Shapeform
Plates
Specifications Thickness
0.187 inches | 4.75 mm
Mechanical Properties Melting Temperature Range
2350 to 2460 ºF | 1290 to 1350 ºC
Mechanical Properties Rupture Strength 1000 H At 1200f65
52000 psi | 360 MPa
Mechanical Properties Rupture Strength 1000 H At 1400f76
23000 psi | 160 MPa
Mechanical Properties Rupture Strength 1000 H At 1600f87
7200 psi | 50 MPa
Mechanical Properties Rupture Strength 1000 H At 1800f98
2600 psi | 18 MPa