Loctite 3D 3843 White HDT60 Semi-Flexible Resin
Loctite 3D 3843 White HDT60 Semi-Flexible Resin
SKU:PRO-f440b6
High-toughness semi-flexible resin with HDT 60°C, superior strength & finish. Ideal for manufacturing needs. Meets ASTM standards.
Regular price
$49.99
Regular price
Sale price
$49.99
Unit price
per
Initiate Order
Loctite 3D 3843 White HDT60 Semi-Flexible Resin
$49.99
Quantity: 1
Claim Your Seller Account
Loctite 3D 3843 White HDT60 Semi-Flexible Resin
$49.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
The Loctite 3D 3843 White HDT60 Semi-Flexible Resin is a high-toughness photoplastic engineered for demanding applications. With a Heat Deflection Temperature of 60°C, this resin offers superior impact strength and excellent surface finish. Ideal for manufacturing aids, jigs, fixtures, housings, and covers, it meets ASTM standards for tensile stress, elongation, flexural modulus, and IZOD impact strength. Its versatility and precise 3D printing capabilities make it a reliable choice for various industries.
Product Specifications
Benefits Benefits
Moderate heat resistance, HDT 60 ºCTough with outstanding surface finishSuperior strength and impact resistant
Liquid Properties Liquid Density
1.07 g/cm³
Liquid Properties Viscosity At 25 Degree Celsius C 77 Degree Fah
450 to 650 cP
Mechanical Properties Green Elongation At Break
74.4 %
Mechanical Properties Green Elongation Tolerance At Break
9.9 %
Mechanical Properties Green Flexural Elongation At Break
>5 %
Mechanical Properties Green Flexural Modulus
721 MPa
Mechanical Properties Green Flexural Modulus Tolerance
36 MPa
Mechanical Properties Green Tensile Stress At Break
33.1 MPa
Mechanical Properties Green Tensile Stress At Yield
36.2 MPa
Mechanical Properties Green Tensile Stress Tolerance At Break
2.6 MPa
Mechanical Properties Green Tensile Stress Tolerance At Yield
1 MPa
Mechanical Properties Green Youngs Modulus
1318 MPa
Mechanical Properties Green Youngs Modulus Tolerance
31 MPa
Mechanical Properties Post Processed Elongation At Break
47.6 %
Mechanical Properties Post Processed Elongation Tolerance At Bre
8 %
Mechanical Properties Post Processed Flexural Elongation At Brea
>5 %
Mechanical Properties Post Processed Flexural Modulus
1673 MPa
Mechanical Properties Post Processed Flexural Modulus Tolerance
44 MPa
Mechanical Properties Post Processed Tensile Stress At Break
49.0 MPa
Mechanical Properties Post Processed Tensile Stress At Yield
52.6 MPa
Mechanical Properties Post Processed Tensile Stress Tolerance At
1 MPa
Mechanical Properties Post Processed Youngs Modulus
1720 MPa
Mechanical Properties Post Processed Youngs Modulus Tolerance
72 MPa
Note Note
All specimen are printed unless otherwise noted. All specimen were conditioned in ambient lab conditions at 19-23ºC / 40-60% RH for at least 24 hours." ASTM Methods: D638 Type IV, 5 mm/min, D790-B, 2 mm/min, D648, D256 Notched IZOD (Machine Notched), 6 mm x 12 mm, D570 0.125" x 2" Disc 24 hr at 25 ºC, D2240, Type "D" (0, 3 seconds), D7867, D1475
Other Properties Green Heat Deflection Temperature Hdt At 0455 M
50 ºC
Other Properties Green Shore Hardness 0s 3s
64 Rockwell D | 68 Rockwell D
Other Properties Green Solid Density
1.18 g/cm³
Other Properties Post Processed Cytotoxicity
Comply
Other Properties Post Processed Heat Deflection Temperature Hdt
60 ºC
Other Properties Post Processed Irritation
Comply
Other Properties Post Processed Izod Impact Strength Notched
58.3 J/m
Other Properties Post Processed Izod Impact Strength Tolerance N
4.2 J/m
Other Properties Post Processed Izod Impact Strength Unnotched
175.3 J/m
Other Properties Post Processed Izod Impact Tolerance Unnotched
12.8 J/m
Other Properties Post Processed Shore Hardness 0s 3s
70 Rockwell D | 76 Rockwell D
Other Properties Post Processed Solid Density
1.18 g/cm³
Specifications Color
White