Durable semi-flexible resin with HDT60 for accurate, high-impact 3D printing. Ideal for manufacturing aids and tooling applications.
Regular price
$89.99
Regular price
Sale price
$89.99
Unit price
per
Initiate Order
Loctite Clear HDT60 Semi-Flexible 3D Resin
$89.99
Quantity: 1
Claim Your Seller Account
Loctite Clear HDT60 Semi-Flexible 3D Resin
$89.99
Quantity: 1
Delivery via Maden
Expect your order to arrive on time.
Secure Payments
All orders are processed through a secure, PCI-compliant checkout.
Loctite Clear HDT60 Semi-Flexible 3D Resin is a high-toughness photoplastic ideal for manufacturing aids, jigs, fixtures, housings, and covers. With a moderate temperature resistance HDT60, it offers exceptional impact strength and a superior surface finish. This engineering plastic ensures accurate printing at room temperature, showcasing high green strength and HDT properties. It meets ASTM standards D638, D790-B, D648, D256, D570, D2240, D7867, and D1475, making it a reliable choice for various industrial applications.
Product Specifications
Benefits Benefits
Moderate heat resistance, HDT 60 ºCTough with outstanding surface finishSuperior strength and impact resistant
Liquid Properties Liquid Density
1.07 g/cm³
Liquid Properties Viscosity At 25 Degree Celsius C 77 Degree Fah
400 to 600 cP
Mechanical Properties Green Elongation At Break
58.0 %
Mechanical Properties Green Elongation Tolerance At Break
24 %
Mechanical Properties Green Tensile Stress At Break
38.0 MPa
Mechanical Properties Green Tensile Stress At Yield
43.8 MPa
Mechanical Properties Green Tensile Stress Tolerance At Break
1.7 MPa
Mechanical Properties Green Tensile Stress Tolerance At Yield
0.7 MPa
Mechanical Properties Green Youngs Modulus
1562 MPa
Mechanical Properties Green Youngs Modulus Tolerance
36 MPa
Mechanical Properties Post Processed Elongation At Break
41.0 %
Mechanical Properties Post Processed Elongation Tolerance At Bre
6.7 %
Mechanical Properties Post Processed Flexural Elongation At Brea
>5 %
Mechanical Properties Post Processed Flexural Modulus
1878 MPa
Mechanical Properties Post Processed Flexural Modulus Tolerance
81 MPa
Mechanical Properties Post Processed Tensile Stress At Break
44.0 MPa
Mechanical Properties Post Processed Tensile Stress At Yield
45.0 MPa
Mechanical Properties Post Processed Tensile Stress Tolerance At
1.5 MPa
Mechanical Properties Post Processed Youngs Modulus
1752 MPa
Mechanical Properties Post Processed Youngs Modulus Tolerance
42 MPa
Note Note
All specimen are printed unless otherwise noted. All specimen were conditioned in ambient lab conditions at 19-23ºC / 40-60% RH for at least 24 hours." ASTM Methods: D638 Type IV, 5 mm/min, D790-B, 2 mm/min, D648, D256 Notched IZOD (Machine Notched), 6 mm x 12 mm, D570 0.125" x 2" Disc 24 hr at 25 ºC, D2240, Type "D" (0, 3 seconds), D7867, D1475
Other Properties Green Solid Density
1.17 g/cm³
Other Properties Post Processed Heat Deflection Temperature Hdt
63 ºC
Other Properties Post Processed Izod Impact Strength Notched
65.0 J/m
Other Properties Post Processed Izod Impact Strength Tolerance N
2.9 J/m
Other Properties Post Processed Shore Hardness 0s 3s
63 Rockwell D | 68 Rockwell D
Other Properties Post Processed Solid Density
1.18 g/cm³
Other Properties Post Processed Water Absorption 24 Hours Hr
2.13 %
Specifications Color
Clear
Specifications Ideal For
Manufacturing aidsJigs and fixturesHousings and coversInsoles
Specifications Markets
Automotive | Consumer Goods | Industry